ASA (Acrylonitrile Styrene Acrylate)

ASA PROPERTIES
Typical Properties	Test Method	Units	ASA 306 UV	ASA 302 UV
IZOD Impact
(12.7 x 3.2mm, notched)	ASTM D256	J/m	300	275
Tensile Strength at 5 mm/min
(12.7 x 3.2mm)	ASTM D638	MPa	40	47
Tensile Modulus at 5 mm/min
(12.7 x 3.2mm)	ASTM D638	MPa	2000
Flexural Strength at 1.3mm/min
(12.7 x 3.2mm)	ASTM D790	MPa	65	76
Flexural Modulus at 1.3mm/min
(12.7 x 3.2mm)	ASTM D790	MPa	2100	2450
Heat Deflection Temp.
(12.7 x 12.7 x 127mm, 1.82 MPa)	ASTM D648	C (unannealed,	88	89
		compression moulded)
Coefficient of Linear Thermal Expansion	ASTM D696	Cm/cm/ C	9.5 x 10-5	9.5 x 10-5
Vicat Softening Point (1 kg)	ASTM D1525	C	105	104
Glow Wire Test Pass Temperature (1.57mm)	AS 2420	C	550	550
Specific Gravity	ASTM D792	-	1.05	1.06
Rockwell Hardness	ASTM D785	R	90	100
Mould Shrinkage	ASTM D955	%	0.5 ± 0.2	0.6 ±0.2

ASA PROPERTIES
Typical Properties	Test Method	Units	797 SE UV	776 SE UV
IZOD Impact
(12.7 x 3.2mm, notched)	ISO 180/1A	KJ/m2	30	15
Tensile Strength at 5 mm/min
(12.7 x 3.2mm)	ISO 527-2	MPa	42	47
Tensile Modulus at 5 mm/min
(12.7 x 3.2mm)	ISO 527-2	MPa	2000	2200
Flexural Strength at 1.3mm/min
(12.7 x 3.2mm)	ISO 178	MPa	60	65
Flexural Modulus at 1.3mm/min
(12.7 x 3.2mm)	ISO 6721-2	MPa	730	800
Heat Deflection Temp.
(12.7 x 12.7 x 127mm, 1.82 MPa)	ISO 75-2	C	95	96
Coefficient of Linear Thermal Expansion
Longitud. (23-80) C	DIN 53752	10-5K	8-11	37203
Vicat Softening Point (1 kg)	ISO 306	C	104	104
Specific Gravity	ASTM D792	-	1.1	1.1

TOLERANCES

Note: All dimensions are measured at 22-24 degrees Celsius.

These figures report reliable and accurate information to the best of our knowledge, however, guarantees cannot be given due to the conditions of use being beyond our control. Sheeting applications should be considered on their merits and, if in doubt, contact Menzel Plastics.